The formation process of cast aluminium components during casting
2026-01-23
Casting cracks represent a particularly detrimental defect, disrupting the continuity of the metallic structure. They cannot be compacted during subsequent extrusion or rolling processes, hence ingots exhibiting cracks are classified as scrap during inspection. The presence of casting cracks significantly impacts the production efficiency and economic performance of aluminium processing enterprises. Consequently, systematic analysis and research into this phenomenon are essential to implement effective measures during production that reduce the occurrence of crack defects and enhance ingot yield rates.